Strength and ductility enhancement of AZ61/Al2O3/SiC hybrid composite by ECAP processing

Song Jeng Huang, Murugan Subramani, Konstantin Borodianskiy

Research output: Contribution to journalArticlepeer-review

32 Scopus citations

Abstract

Magnesium is a low-density metal which is used in extensive structural applications such as load-bearing components in the automobile industry. To improve the strength and ductility of the magnesium alloys, method of production of metal matrix composites have been developed. In this study, AZ61 magnesium alloy was reinforced with hybrid particles (2 wt% Al2O3 and 1 wt% SiC) fabricated by the stir casting method. Then, the casted samples were homogenized at 410 °C for 24 h, aged at 200 °C for 10 h followed by severe plastic deformation (SPD) processing using equal channel angular pressing (ECAP). The obtained microstructure observation showed that the hybrid reinforcement particles were uniformly distributed in the metal matrix. After the ECAP process, the grain size was significantly reduced from 148.79 ± 79 µm to 12.2 ± 8 µm due to the dynamic recrystallization (DRX) mechanism during the plastic deformation. The mechanical properties of hardness, yield strength (YS), ultimate tensile strength (UTS), and elongation are effectively improved after each ECAP pass; the maximum values achieved were 61.2 ± 4.6 HV, 110.3 MPa, 250.1 MPa, and 19.3%, respectively on the AZ61/Al2O3/SiC hybrid composite subjected to two passes of ECAP. The enhancement of the mechanical properties of the AZ61 hybrid composites was mainly attributed to the Hall-Petch strengthening mechanism.

Original languageEnglish
Article number103261
JournalMaterials Today Communications
Volume31
DOIs
StatePublished - Jun 2022
Externally publishedYes

Bibliographical note

Publisher Copyright:
© 2022 Elsevier Ltd

Funding

M.S. would like to thank a Ph.D. Sandwich Scholarship Program provided by a Council for Higher Education of Israel for the support in this work.

FundersFunder number
Council for Higher Education

    Keywords

    • ECAP processing
    • Hybrid composite
    • Mg alloy
    • Stir casting

    Fingerprint

    Dive into the research topics of 'Strength and ductility enhancement of AZ61/Al2O3/SiC hybrid composite by ECAP processing'. Together they form a unique fingerprint.

    Cite this