Oxygen content and crystallinity effects in pulsed laser deposited lanthanum manganite thin films

S. V. Pietambaram, D. Kumar, R. K. Singh, C. B. Lee

Research output: Contribution to journalConference articlepeer-review

4 Scopus citations


Eventhough colossal magnetoresistance in Lanthanum calcium manganite (LCMO) thin films was known for a long time, the effect of oxygen content and crystallinity on the properties of these films is not clearly understood. It is in this context that we have performed a systematic study of these effects by annealing the films in various ambients. A series of LCMO thin films have been grown in situ on (100) LaAlO3 substrates using a pulsed laser deposition technique under identical conditions. Microstructural characterization carried out on these films has shown that the films are smooth, single phase and highly textured. The films were subjected to the following post deposition treatments: (i) annealing in oxygen at 900°C for 4 hrs, (ii) annealing in argon at 900°C for 4 hrs, (iii) annealing in oxygen at 500°C for 12 hrs, (iv) annealing in argon for 12 hrs and (v) annealing in vacuum at 850°C for half-an-hour. As deposited LCMO films show a transition temperature of 260 K and a magnetoresistance ratio (defined as [R(0)R(H)/R(H)]) of 190% at 260 K in 5T magnetic field. The samples subjected to 500°C oxygen and Ar anneal have shown no change in the transition temperature and MR ratio. The films subjected to a 900°C annealing in Ar ambient have shown marginal improvement in transition temperature but a drastic improvement in the MR ratio (525%). 900°C oxygen annealed films have shown an improvement in the transition temperature (290 K) and MR ratio (225%) over as deposited films. Vacuum annealed samples have shown deteriorated properties. These results indicate that the metal-insulator transition is related to the oxygen content of the films while the MR ratio is related to the domain size.

Original languageEnglish
Pages (from-to)J3141-J3146
JournalMaterials Research Society Symposium - Proceedings
StatePublished - 2000
Externally publishedYes
EventLaser-Solid Interactions for Materials Processing - San Francisco, CA, United States
Duration: 25 Apr 200027 Apr 2000


Dive into the research topics of 'Oxygen content and crystallinity effects in pulsed laser deposited lanthanum manganite thin films'. Together they form a unique fingerprint.

Cite this